Items		Method	Condition	Unit	Typical Value
Tg		IPC-TM-650 2.4.25	DSC	℃	155
Td		IPC-TM-650 2.4.24.6	5% wt. loss	℃	355
CTE (Z-axis)		IPC-TM-650 2.4.24	Before Tg	ppm/℃	40
			After Tg	ppm/℃	230
			50-260℃	%	2.8
T260		IPC-TM-650 2.4.24.1	TMA	min	>60
T288		IPC-TM-650 2.4.24.1	TMA	min	>60
Thermal Stress		IPC-TM-650 2.4.13.1	288℃, solder dip	s	>100
Volume Resistivity		IPC-TM-650 2.5.17.1	C-96/35/90	MΩ.cm	1.15E+08
Surface Resistivity		IPC-TM-650 2.5.17.1	C-96/35/90	MΩ	9.61E+06
Arc Resistance		IPC-TM-650 2.5.1	D-48/50+D-4/23	s	178
Dielectric Breakdown		IPC-TM-650 2.5.6	D-48/50+D-4/23	kV	>45
Permittivity (1GHz)		IPC-TM-650 2.5.5.9	C-24/23/50	--	4.5
Loss Tangent (1GHz)		IPC-TM-650 2.5.5.9	C-24/23/50	--	0.011
Peel Strength (1 oz)		IPC-TM-650 2.4.8	288℃,10s	N/mm[lb/in]	1.5[8.57]
Flexural Strength	LW	IPC-TM-650 2.4.4	A	MPa	630
	CW	IPC-TM-650 2.4.4	A	MPa	480
Water Absorption		IPC-TM-650 2.6.2.1	D-24/23	%	0.1
Flammability		UL94	C-48/23/50	Rating	V-0
CTI		IEC 60112	A	Grade	PLC 1*

Remarks:

1. Specification sheet: IPC-4101/128, is for your reference only.

2. All the typical value is based on the 1.6mm specimen, while the Tg is for specimen≥0.50mm.

3. All the typical values listed above are for your reference only and not intended for specification. Please contact Shengyi Technology Co., Ltd. for detailed information. All rights from this data sheet are reserved by Shengyi Technology Co., Ltd.

Explanation: C=Humidity conditioning, D=Immersion conditioning in distilled water, E=Temperature conditioning

The first digit following the letter indicates the duration of preconditioning in hours, the second digit the preconditioning temperature in ℃ and the third digit the relative humidity.